The studies are focused on the properties of the multilayer composite coating based on the (Ti,Y,Al)N system with high content of yttrium (about 40 at.%) of yttrium (Y). The hardness and elastic modulus were defined, and the resistance to fracture was studied during the scratch testing. Two cubic solid solutions (fcc phases), including c-(Ti,Y,Al)N and c-(Y,Ti,Al)N, are formed in the coating. The investigation of the wear resistance of the (Ti,Y,Al)N-coated tools during the turning of steel in comparison with the wear resistance of the tools with the based on the (Ti,Cr,Al)N system coating and the uncoated tools found a noticeable increase (by 250%–270%) in rake wear resistance. Active oxidation processes are observed in the (Ti,Y,Al)N coating during wear. It can be assumed that yttrium oxide is predominantly formed with a possible insignificant formation of titanium and aluminum oxides. At the same time, complete oxidation of c-(Y,Ti,Al)N nanolayers is not observed. Some hypotheses explaining the rather high performance of a coating with a high yttrium content are considered.

No abstract

No abstract

No abstract

No abstract