Mechanical properties of dissimilar metal of spot welding were tested and analyzed based on the variation in welding currents and welding times. From visual observation, the largest weld nugget recorded was 7.43 mm at 5 kA, meanwhile the smallest was 6.4 mm at 3 kA. It was found that weld nugget size increase with the increment of weld current and extension of weld time. Based on tensile result, the largest weld nugget size of 7.43 mm produced the highest tensile strength, 31.99 N/mm2 mean while the smallest weld nugget 6.4 mm produced 29.40 N/mm2. The results show that weld nugget size affect the tensile shear strength, and with the increment of weld current and extension of welding time, tensile shear strength increase. Dynamic mechanical properties defined the storage modulus, loss modulus and damping capacity of dissimilar metal spot welded. It was found that at 10 Hz frequency between 70°C to 350°C, with heating rate of 10°C/minute, the storage modulus increase with increment in weld current and the extension of weld time to 8 s. Meanwhile the loss modulus decrease with the increased of weld current and weld time. Same pattern happen to damping capacity, the value dropped with the increases of welding current and welding time.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.