Organic semiconductors with higher carrier mobility and better transparency have been actively pursued for numerous applications, such as flat-panel display backplane and sensor arrays. The carrier mobility is an important figure of merit and is sensitively influenced by the crystallinity and the molecular arrangement in a crystal lattice. Here we describe the growth of a highly aligned meta-stable structure of 2,7-dioctyl[1]benzothieno [3,2-b][1]benzothiophene (C8-BTBT) from a blended solution of C8-BTBT and polystyrene by using a novel offcentre spin-coating method. Combined with a vertical phase separation of the blend, the highly aligned, meta-stable C8-BTBT films provide a significantly increased thin film transistor hole mobility up to 43 cm 2 Vs À 1 (25 cm 2 Vs À 1 on average), which is the highest value reported to date for all organic molecules. The resulting transistors show high transparency of 490% over the visible spectrum, indicating their potential for transparent, high-performance organic electronics.

We introduce a novel siloxane-terminated solubilizing group and demonstrate its effectiveness as a side chain in an isoindigo-based conjugated polymer. An average hole mobility of 2.00 cm(2) V(-1) s(-1) (with a maximum mobility of 2.48 cm(2) V(-1) s(-1)), was obtained from solution-processed thin-film transistors, one of the highest mobilities reported to date. In contrast, the reference polymer with a branched alkyl side chain gave an average hole mobility of 0.30 cm(2) V(-1) s(-1) and a maximum mobility of 0.57 cm(2) V(-1) s(-1). This is largely explained by the polymer packing: our new polymer exhibited a π-π stacking distance of 3.58 Å, while the reference polymer showed a distance of 3.76 Å.