The compression creep behavior was studied for the ternary solder alloy 95.5Sn-3.9Ag-0.6Cu in the as-cast condition. Samples were tested under stresses of 2-45 MPa and temperatures of Ϫ25-160°C. There was a significant variability in the creep curve shape, strain magnitude, and steady-state strainrate properties. A multivariable linear-regression analysis of the steady-state strain-rate data, using the sinh-law stress representation, indicated two mechanisms distinguished by low-and high-temperature regimes of Ϫ25-75°C and 75-160°C, respectively. The sinh-law stress exponent (n) and apparentactivation energy (∆H) in the Ϫ25-75°C regime were 4.4 Ϯ 0.7 kJ/mol and 25 Ϯ 7 kJ/mol (63% confidence intervals), respectively. Those same parameters in the 75-160°C regime were 5.2 Ϯ 0.8 kJ/mol and 95 Ϯ 14 kJ/mol, respectively, for the high-temperature regime. The values of ∆H suggested a short-circuit diffusion mechanism at low temperatures and a lattice or bulk-diffusion mechanism at high temperatures. The stress dependency of the steady-state strain rate did not indicate a strong power-law breakdown behavior or a threshold stress phenomenon. Cracks and grain-boundary sliding were not observed in any of the samples. As the creep temperature increased, a coarsened particle boundary and particle depletion zone formed in the region of fine Ag 3 Sn particles that existed between the Sn-rich phase areas. The coarsened particle boundary, as well as accelerated coarsening of Ag 3 Sn particles, were direct consequences of the creep deformation process.
Compression creep tests were performed on the 95.5Sn-3.9Ag-0.6Cu (wt.%) solder. The specimens were aged prior to testing at 125°C, 24 h or 150°C, 24 h. Applied stresses were 2-40 MPa. Test temperatures were Ϫ25°C to 160°C. The 125°C, 24-h aging treatment caused the formation of coarsened Ag 3 Sn particle boundaries within the larger ternary-eutectic regions. The 150°C, 24-h aging treatment resulted in contiguous Ag 3 Sn boundaries in the ternary-eutectic regions as well as a general coarsening of Ag 3 Sn particles. The 125°C, 24-h aging treatment had only a small effect on the strain-time curves vis-à-vis the as-cast condition. Negative creep was observed at 75°C for time periods Ͼ10 5 sec and stresses of 3-10 MPa. The creep kinetics exhibited a sinh term (stress) exponent, p, of 5.3 Ϯ 0.6 and an apparent-activation energy, ∆H, of 49 Ϯ 5 kJ/mol when data from all test temperatures were included. A good data correlation was observed over the [Ϫ25-125°C] temperature regime. Steady-state creep kinetics exhibited a greater variability in the [125-160°C] regime because of the simultaneous coarsening of Ag 3 Sn particles. The aging treatment of 150°C for 24 h resulted in a more consistent stress dependence and better reproducibility of the creep curves. Negative creep was observed in samples aged at 150°C for 24 h when tested at Ϫ25°C, 25°C, and 75°C. The values of p and ∆H were 4.9 Ϯ 0.3 kJ/mol and 6 Ϯ 5 kJ/mol, respectively. Only a slight improvement in the data correlation was observed when the analysis examined separated [Ϫ25-75°C] and [75-166°C] temperature regimes. Creep testing did not cause observable deformation in any of the sample microstructures.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.