LaCaBaCu 3 O 7 (La1113) is a superconductor below T C(onset) =80K and its structure is similar to the tetragonal YBCO. In this work the magnetic properties of a bulk La1113 sample are reported and compared to those of YBCO superconductor. We explore a possibly relation of this property to its particular crystalline structure, particularly to the oxygen deficiency. In contrast to a bulk YBCO, some magnetic characteristics of La1113 below T C are: the magnetic flux can penetrate easily the bulk in its vortex region (H C1
In this work we present the results about the preparation of the superconductor YBa2Cu3O7-δ (Y123) by sol-gel method using oxalate precursors. Samples were prepared by dissolving stoichiometric mixtures of Y(OOCCH3).4H2O, Ba(OOCCH3)2 and Cu(OOCCH3)2.H2O acetates in aqueous solution of oxalic acid, HCOO-COOH. The particulate sols obtained (2g.) were divided in two parts (1g. each one), from which the first one (sample A) was grinded, pellet, calcined (860°C) and sinterised at 860°C in oxidizing atmosphere, the second part (sample B) was grinded, pellet, calcined at 880°C and finally sinterized at 880°C in the same conditions, the XRD revels the superconductor Y123 is formed in the first sample, but coexisting with remarkable presence of the secondary phases: CuO, BaCu3O4, BaCO3 and BaCuO2, while in sample B the XRD reveals the obtention of high purity monophase Y123, the ac susceptibility measurement using a Quantum Design (SQUID) magnetometer indicates TC(onset)=92K for this sample, moreover the Rietveld refinement was done taking the orthorhombic Pmmm Y123 spatial group as a model, this suggest the cell´s parameters a=3.839Å, b=3.899 Å and c=11.702Å as reported in the literature. Therefore for the preparation of Y123-superconductor using oxalate precursors, the optimus sintering temperature is 880°C.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.