Battery-type electrode materials have attracted much attention as efficient and unique types of materials for hybrid battery supercapacitors due to their multiple redox states and excellent electrical conductivity. Designing composites with high chemical and electrochemical stabilities is beneficial for improving the energy storage capability of battery-type electrode materials. We report on an interfacial engineering strategy to improve the energy storage performance of a Co(OH)2-based battery-type material by constructing polypyrrole-assisted and Ag-doped (Ag-doped@Co(OH)2@polypyrrole) nanosheets (NSs) on a Ni foam using a hydrothermal process that provides richer electroactive sites, efficient charge transportation, and an excellent mechanical stability. Physical characterization results revealed that the subsequent decoration of Ag nanoparticles on Co(OH)2 nanoparticles offered an efficient electrical conductivity as well as a reduced interface adsorption energy of OH- in Co(OH)2 nanoparticles as compared to Co(OH)2@polypyrrole-assisted nanoparticles without Ag particles. The heterogeneous interface of the Ag-doped@Co(OH)2@polypyrrole composite exhibited a high specific capacity of 291.2 mAh g−1 at a current density of 2 A g−1, and showed a good cycling stability after 5000 cycles at 5 A g−1. The specific capacity of the doped electrode was enhanced approximately two-fold compared to that of the pure electrode. Thus, the fabricated Ag-doped@Co(OH)2@polypyrrole nanostructured electrodes can be a potential candidate for fabricating low-cost and high-performance energy storage supercapacitor devices.

Transition-metal sulfides exaggerate higher theoretical capacities and were considered a type of prospective nanomaterials for energy storage; their inherent weaker conductivities and lower electrochemical active sites limited the commercial applications of the electrodes. The sheet-like nickel cobalt sulfide nanoparticles with richer sulfur vacancies were fabricated by a two-step hydrothermal technique. The sheet-like nanoparticles self-combination by ultrathin nanoparticles brought active electrodes entirely contacted with the electrolytes, benefiting ion diffusion and charges/discharges. Nevertheless, defect engineers of sulfur vacancy at the atomic level raise the intrinsic conductivities and improve the active sites for energy storage functions. As a result, the gained sulfur-deficient NiCo2S4 nanosheets consist of good specific capacitances of 971 F g−1 at 2 A g−1 and an excellent cycle span, retaining 88.7% of the initial capacitance over 3500 cyclings. Moreover, the values of capacitance results exhibited that the fulfilling characteristic of the sample was a combination of the hydrothermal procedure and the surface capacitances behavior. This novel investigation proposes a new perspective to importantly improve the electrochemical performances of the electrode by the absolute engineering of defects and morphologies in the supercapacitor field.