The research is aimed to investigate the possibility of acrylic-reinforced glass fibre as a denture. Short glass fibre was made by variation of 4mm, 6 mm and 8mm. The results showed a good adhesion between glass fibre and acrylic resin with an optimum composition of the denture (acrylic: oil : glass fibre = 10 gr : 4.5 mL : 0.13 gr) was achieved. The density test was conducted by using Archimedes' method, whereas compressive strength and tensile strength by using Universal Testing Machine (UTM). The results showed that glass fibre can be used to enhance the mechanical properties of acrylic resin. The optimum composition was achieved when 6 mm fibre had been added-in with a density of 1.2256 gr/cm 3 . A compressive strength of 76.623 MPa and a tensile strength of 71.207 MPa were recorded, these values can be applied as a denture.

No abstract

Research has been carried out regarding the manufacturing process of polymer concrete made from a mixture of pumice, sand (1: 1), corn husk fiber, epoxy and thinner resin. This research was conducted to determine the characterization of polymer concrete which will be tested physically and mechanically with the best composition mixture. The physical properties of polymer concrete which were analyzed namely density, porosity and water absorption; mechanical properties including impact strength, flexural strength and compressive strength, and polymer concrete microstructure analysis, namely SEM-EDX. The best results were obtained with a mixture of pumice, sand (1:1), corn husk fiber, epoxy and thinner resin. The result are as stated here, density: 1.84 g/cm3 with composition (49:49:2) 30 g epoxy resin, porosity : 0.44% with composition (50:50:0) 20 g epoxy resin, water absorption: 1.8% with composition (50:50:0) 25 g of epoxy resin. Whereas mechanical properties, on impact tests: 4.956 KJ/m2 with composition of (47:47:6) 25 g epoxy resin, flexural test: 22.22 MPa with composition of (45:45:0) 30 g epoxy resin, pressure test: 8.41 MPa with composition of (49:49:2) 30 g epoxy resin. XRD analysis shows that each of its constituents still have quartz, pumice, quartz, pumice-shaped hexagonal crystals, while corn husk fibers are amorphous crystals. The average sound absorption coefficient for the three samples (20%, 25%, and 30%) are 0.178; 0.152; and 0.234 at a frequency of 500 Hz - 6300 Hz, which meets the requirements of ISO 11654 and ASTM C.384.

No abstract