Hypereutectic Al - Si alloys with fine and evenly distributed Si precipitates have superior mechanical properties In this study, hypereutectic Al - Si alloy powders which contained 15 and 20wt% Si were prepared by a gas atomization process. 1, 3 and 5wt% AlN particles were blended with the Al - Si alloy powders using turbular mixer. The mixture was consolidated by Hot Press at 550°C for 1h under 60MPa. Relative density of the sintered samples was about 98% of theoretical density. This study was investigated by two ways. One is the effect of reinforcement weight fraction and the other is the effect of Silicon contents on the mechanical properties of the composite. Microstructural characterization and phase evaluation were carried out using X-ray Diffraction, Scanning Electron Microscopy equipped with Energy Dispersive Spectrometer. The results showed that the smaller the reinforcement particle size was and the better its distribution was, the higher ultimate tensile strength and hardness were.

This study examined the effects of CSR characteristics on company image, CSV, customer satisfaction, customer citizenship behavior for customers using mobile phones of Samsung, LG, Apple, and Pantech in domestic market. 213 questionnaire samples are used to test 10 hypotheses using structural equation model with AMOS. Results of testing are as follows: First, economic responsibilities, law-ethical responsibilities and philanthropic responsibilities factors of CSR influence positively to company image. Second, economic responsibilities does not influence to CSV. Third, company image influence positively to customer satisfaction and customer citizenship behavior, but CSV does not influence to customer satisfaction This study shows that CSR, company image, CSV are important for customers' increasing customer satisfaction and customer citizenship behavior. Implications and limitations of this study also suggested.

No abstract