For a lamella-forming poly(ethylene oxide)-block-polystyrene (PEO-b-PS) diblock copolymer (M h n PEO ) 8.7K and M h n PS ) 9.2K), the glass transition temperature of the PS blocks is 62 °C, and the melting temperature of the PEO crystals is around 51 °C when the sample is crystallized below 40 °C. The PEO blocks thus crystallize in a one-dimensionally confined lamellar space of 8.8 nm, as studied recently by one-dimensional small-angle X-ray scattering (SAXS) and transmission electron microscopy. In this report, the crystal orientation (the c-axis of the PEO crystals) within nanoscale confined lamellae has been investigated using combined two-dimensional SAXS and wide-angle X-ray scattering experiments. The c-axis orientation in the PEO crystals is observed for the first time to change from random to perpendicular, then to inclined, and finally to parallel to the lamellar surface normal, depending only on the crystallization temperature (T c ). Detailed crystallographic analyses indicate that the c-axis orientation at each T c corresponds to a uniform orientation rather than a mixture of different crystal orientations.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.