Aim The aim of this study was to see the effect of topical fluoride on surface texture on nickel-titanium and copper-nickel-titanium orthodontic archwires. Materials and methods Preformed rectangular NiTi and CuNiTi wires were immersed in in fluoride solution and artificial saliva (control) for 90 minutes at 37°C. after immersion optical microscope was used to see the fluoride effect on the wire topography. Results The acidulated fluoride agents appeared to cause greater corrosive effects as compared to the neutral fluoride agents. Conclusion The result suggest that using topical fluoride agents leads to corrosion of surface topography indirectly affecting the mechanical properties of the wire that will lead to prolonged orthodontic treatment. Clinical significance The use of topical fluoride agents has to be limited in patients with prolonged orthodontic treatment as it causes the corrosion of the NiTi and CuNiTi wires. How to cite this article Mane PN, Pawar R, Ganiger C, Phaphe S. Effect of Fluoride Prophylactic Agents on the Surface Topography of NiTi and CuNiTi wires. J Contemp Dent Pract 2012;13(3):285-288.

No abstract

Introduction: After debonding, white spot may appear on the area below the bracket, which is the early clinical sign of carious lesion. There is increased caries risk underneath and adjacent to orthodontic bands and brackets, which call for maximum use of caries preventive procedures using various fluoride application methods. Objective: The aim of the study was to evaluate alterations in the mechanical properties (modulus of elasticity and yield strength) in loading and unloading phases for different orthodontic archwires (nickel-titanium [NiTi] and copper-nickel-titanium [CuNiTi]) when exposed routinely to fluoride prophylactic agents for a predetermined period of time. Methods: Preformed rectangular NiTi and CuNiTi wires were immersed in fluoride solution and artificial saliva (control) for 90 minutes at 37ºC. After immersion, specimens were tested using a 3-point bend test on a universal testing machine. Results: There is a significant reduction in the unloading yield strength when the NiTi and CuNiTi wires were exposed to APF gel. Conclusion: The result suggests that use of topical fluoride agents affect the mechanical properties of the wires, leading to increase in treatment duration. Fluoride prophylactic agents must be used with caution in patients undergoing orthodontic treatment. Injudicious use of these agents may cause corrosive effects on the orthodontic wire surfaces, with alteration in their mechanical properties.

Aim This study was undertaken to analyze the clinical usefulness of the maxillomandibular bisector, its reproducibility, its validity and its relationship to the functional occlusal plane, the bisecting occlusal plane and the nature of its cant. Materials and methods Thirty pretreatment lateral cephalograms, each of adolescents (above 18 years of age) and children (10- 12 years), seeking orthodontic treatment were randomly selected and the Wits technique of anteroposterior measurement was used to compare A-B values measured to the new plane with those measured to the functional occlusal plane (FOP) and to the traditional or bisecting occlusal plane (BOP). Results Present study showed that MM bisector plane is more reproducible and valid reference plane, than the FOP and BOP. Conclusion A new plane, geometrically derived from the dental base planes, has been tested as an occlusal plane substitute for the measurement of anteroposterior jaw relationships. It lies close to but at an angle and inferior to the traditional occlusal planes and is highly reproducible at all times. Clinical significance Maxillomandibular planes angle bisector may be a useful adjunct for the cephalometric assessment of sagittal relationship of the patient. How to cite this article Ganiger CR, Nayak USK, Cariappa KU, Ahammed ARY. Maxillomandibular Plane Angle Bisector (MM) Adjunctive to Occlusal Plane to evaluate Anteroposterior Measurement of Dental Base. J Contemp Dent Pract 2012; 13(4):539-544.