This study reported the preparation and characterization of gel polymer electrolyte (GPE) using poly (vinylidine fluoride-co-hexafluoropropylene) (PVdF-HFP), lithium perchlorate (LiClO4) and 1-butyl-3-metilimmidazoliumhexafluorophosphate [PF6]. The GPE were prepared by solution casting technique. [Bmim] [PF6] ionic liquid is used as an additive for the purpose of increasing the ionic conductivity of GPE. Morphological analysis showed that the electrolyte gel polymer sample had a smooth and flat surface with the addition of [Bmim] [PF6] and no phase separation effect was observed. This shows the compatibility between PVdF-HFP and [Bmim] [PF6]. ATR-FTIR analysis showed that C-F bond related peaks experienced peak changes in terms of intensity and peak shifting. This proves the interaction of the imidazolium ion with the fluorine atom through the formation of coordinate bonds. Ionic conductivity analysis showed that PVdF-HFP-[Bmim][PF6] samples reached a maximum room temperature ionic conductivity value of 2.44 × 10-4 S cm-1 at 60 wt.% [Bmim] [PF6]. When 20 wt.% of LiClO4 added to the system, the ionic conductivity increased one magnitude order to 2.20 × 10-3 S cm-1.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.