The combination of strength of transformation-induced plasticity (TRIP) steel and ductility of twinning-induced plasticity (TWIP) steel can be achieved by manufacturing laminated composites via cold roll bonding (CRB). Work hardening of the surface before CRB produces deformation lenses (DLs), which play significant role in bonding, but are reported rarely in the literature. The present work aimed to study the DLs at the bonding interface of the laminated composite made of high-alloy TRIP and TWIP steels manufactured by CRB. The DLs and interfaces were investigated by means of scanning and transmission electron microscopy, roughness measurement, tensile and peel tests. Laminates showed ultimate tensile strength up to 900 MPa and elongation up to 45% maintaining the layer’s integrity up to failure. The TWIP–TWIP interface has shown higher maximum peel strength (up to 195 N/cm) than that of a TRIP–TWIP interface (up to 130 N/cm), which was found to be in direct proportion to the overall area of DLs. Bonding of the laminate layers was found to occur between DL fragments.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.