Oxygen overlayer / Dissolved oxygen / Fitting interstitial sites / Silver oxide decomposition Silver under ambient conditions is always covered at least with adsorbed atomic oxygen and coadsorbed C02, and at 300 the low susceptibility of the metal to oxidation may thus be assigned to the existence of this overlayer. At elevated temperatures surface species are desorbed without leading to a higher reactivity of Ag. Our experiments showed that under these conditions in the presence of 02 large amounts of dissolved oxygen are formed, and this species proved to be hard to remove either thermically or by heating the sample in hydrogen. According to the structural conditions of the silver lattice atomic oxygen fits perfectly into the octahedral holes so that dissolution is possible with hardly changing the atomic distances.Unter normalen Umgebungsbedingungen ist Silber stets bedeckt zumindest mit atomar adsorbiertem Sauerstoff und koadsorbiertem C02; die geringe Oxidationsneigung des Metalls bei 300 C kann dieser Obcrflächcnschicht zugeschrieben werden. Bei höheren Temperaturen desorbieren die Oberflächenspezics. doch nimmt dadurch die Reaktivität des Ag nicht zu. Wie unsere Untersuchungen zeigten, werden unter diesen Bedingungen in Gegenwart von 02 große Mengen von Sauerstoff gelöst, die thermisch oder durch Aufheizen unter Wasserstoff nur schwer zu entfernen sind. In der Gitterstruktur des Silbers paßt atomarer Sauerstoff präzise in die Oktaederlücken, so daß sich bei der Einlagerung die Atomabstände kaum zu ändern brauchen.

No abstract

No abstract