Styrenedivinylbenzene macroporous resins were prepared with the same composition (13% DVB), but varying diluent amount of benzyl alcohol. From sample analysis, the copolymerization kinetics concerning both monomer consumption and residual double bond amount were determined. Porous texture and morphology analyses by BET**, BJH***, mercury porosimetry, and scanning electron microscopy were carried out, too. Depending on diluent amount, the final product is classified as inside or outside the macroporous domain. Texture evolution is clearly different for the two classes of products, although their chemical evolutions are almost the same. A qualitative discussion of porous texture formation is presented, based on occurrence of three critical events: gelation, phase separation and molecular overlap. ZUSAMMENFASSUNG:Es wurden makropor6se Styrol-Divinylbenzol-Harze bei gleicher Zusammensetzung (1 3% Divinylbenzol), aber mit variierenden Verdiinnunganteilen von Benzylalkohol, hergestellt. Aus der Analyse der Proben wurde die Copolymerisationskinetik sowohl aufgrund des Monomerverbrauchs als auch des Doppelbindungsanteils bestimmt. Ebenso wurden Porenstruktur-und Morphologieanalysen mittels BET, BJH, Quecksilberporosimetrie und Rasterelektronenmikroskopie durchgefiihrt. In Abhtingigkeit vom Anteil an Verdiinnungsmittel wurde das Endprodukt als innerer oder ilu-Derer makropor0ser Bereich klassifiziert. Die Strukturbildung ist fur die zwei Produktklassen unterschiedlich, obwohl ihre chemische Entstehung nahezu gleich ist. Es wird eine qualitative Diskussion iiber die Bildung der lockeren Struktur gegeben, die auf drei kritischen Erscheinungen beruht: Gelbildung, Phasentrennung und molekulare Uberlappung.