Porous poly(vinyl alcohol) (PVA)/sepiolite nanocomposite scaffolds containing 0-10wt.% sepiolite were prepared by freeze-drying and thermally crosslinked with poly(arylic acid).The microstructure of the obtained scaffolds was characterised by scanning electron microscopy and micro computer tomography, which showed a ribbon and ladder like interconnected structure. The incorporation of sepiolite increased the mean pore size and porosity of the PVA scaffold as well as the degree of anisotropy due to its fibrous structure.The tensile strength, modulus and energy at break of the PVA solid material that constructed the scaffold were found to improve with additions of sepiolite by up to 104%, 331% and 22% for 6wt.% clay. Such enhancements were attributed to the strong interactions between the PVA and sepiolite, the good dispersion of sepiolite nanofibres in the matrix and the intrinsic properties of the nanofibres. However, the tensile properties of the PVA scaffold deteriorated in the presence of sepiolite because of the higher porosity, pore size and degree of anisotropy.The PVA/sepiolite nanocomposite scaffold containing 6wt.% sepiolite was characterized by an interconnected structure, a porosity of 89.5% and a mean pore size of 79μm and exhibited a tensile strength of 0.44MPa and modulus of 14.9MPa, which demonstrates potential for this type of materials to be further developed as bone scaffolds.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.