Fluorine-containing poly(benzoxazinone-imide)s and poly(benzoxazinone-phenylquinoxaline-imide-amide)s have been synthesized by solution polycondensation of diacid dichlorides containing imide and hexafluoroisopropylidene groups with 4,4'-diaminodiphenylmethane-3,3'-dicarboxylic acid or with mixtures of the latter with a diamino phenylquinoxaline. These polymers show high thermal stability, the decomposition temperatures being in the range of 450-470°C.Transparent flexible films were cast from the solutions of the corresponding polyamidic acid intermediates that after thermal cyclization showed low dielectric constant which recommends them for future applications in microelectronics. ZUSAMMENFASSUNG:Fluorhaltige Poly(benzoxazinon-imid)e und Poly(benzoxazinonphenylchinoxa1inimid-amid)e wurden mittels Liisungspolykondensation von Imid-und Hexafluorisopropylidengruppen enthaltenden Dicarbonsauredichloriden mit 4,Q-Diaminodiphenylmethan-3,3'-dicarbonsaure oder Mischungen des letzteren mit Diaminophenylchinoxalinen hergestellt. Die Polymeren besitzen eine hohe thermische Stabilitat mit Zersetzungstemperaturen im Bereich 450-470 "C.Aus den Losungen der entsprechenden Polyamidsauren wurden Filmen gegossen, die nach thermischer Cyclisierung geringe Dielektrizitatskonstanten aufwiesen, was sie fur die Anwendung in der Mikroelektronik geeignet erscheinen 1aBt.

The effect of three organophosphonic compounds on the thermooxidative degradation of the uncured diglycidyl ether-bisphenol-A epoxy resin was investigated, using infrared spectroscopy, thermogravimetry, differential thermogravimetry, static pyrolysis, pyrolysis-gas chromatography and elemental analysis. The results obtained indicate that additives with phosphorus and chlorine or nitrogen in molecules exercise an influence upon the degradative process of uncured resin by catalysing its decomposition in the lower temperature region. At the same time, the tested additives promote the formation of highly thermostable and non-flammable structures in the solid residue. ZUSAMMENFASSUNG:Der Einflufi von drei organischen, phosphorhaltigen Verbindungen auf die thermooxidativen Eigenschaften eines ungeharteten Epoxidharzes, einen Diglycidylether von Bisphenol-A, wurde mittels IR-Spektroskopie, Thermogravimetrie, Differentialthermogravimetrie, statischer Pyrolyse, Pyrolyse-Gaschromatographie und Elementaranalyse untersucht. Die Ergebnisse deuten darauf hin, dal3 Additive mit Phosphor und Chlor oder Stickstoff im Molekul den Abbauprozefi des ungeharteten Harzes bei niedrigeren Temperaturen begiinstigen und gleichzeitig zur Bildung thermostabiler und nicht brennbarer Strukturen im festen Ruckstand beitragen.