We studied the effects of gamma irradiation on the dimensions, mechanical and material properties, and mature hydroxypyridinium crosslink density of collagen in goat patellar tendon-bone specimens. Left and right patellar tendon-bone units were removed from 10 adult female goats and were bisected longitudinally. Each tendon half was frozen, and then the left halves were exposed to 4, 6, or 8 Mrad (40,000, 60,000, or 80,000 Gy) of gamma irradiation. The contralateral tendon halves served as controls (no irradiation). Each specimen then was loaded to failure in tension, and its soft-tissue midsubstance was processed to measure collagen content and hydroxypyridinium crosslink density. Dose-dependent reductions in the mechanical properties were found, including 46% (p < 0.01) and 18% (p < 0.05) reductions in maximum force and stiffness, respectively, at 4 Mrad. Similar reductions were noted in material properties, including 37% (p < 0.005) and 8% (p > 0.05) reductions in maximum stress and modulus, respectively, at 4 Mrad. These results are consistent with our previous report involving 2 and 3 Mrad (20,000 and 30,000 Gy) of exposure. We also found significant decreases in hydroxypyridinium crosslink density with 6 Mrad of irradiation (p < 0.05). However, since only one biomechanical parameter (modulus) correlated significantly with only one biochemical measure (hydroxypyridinium crosslink density) (p < 0.05), other possible mechanisms also are being explored to more fully explain these dose-dependent changes.

Background: High levels of gamma irradiation are required to eliminate the risk of bacterial and viral transmission during implantation of musculoskeletal allografts. The effects of high levels of gamma irradiation on anterior cruciate ligament allograft biomechanics are still not known.

No abstract

No abstract