The nature of the yield zone at the crack tip of poly(vinyl chloride) (PVC) pipe materials has been investigated. Microscopy studies employing a plasma etching technique reveal the presence of multiple crazes ahead of the crack tip in the interior of specimens of pure PVC, CaCO3 filled PVC, and PVC pipe compound. The craze zone and the fracture toughness of blade‐notched specimens are compared with those of fatigue pre‐cracked specimens. Both types of specimens have similar fracture toughness values and form multiple crazes upon loading, suggesting that multiple crazing Is an intrinsic property of the material. The kinetics of craze initiation and the development of the multiple craze zones have also been explored.