The creep-rupture behaviour of steel X6 CrNi 18 ii (type AISI 304) is influenced by the presence of very pure liquid sodium at 550 C. Creep-rupture tests in a sodium loop have shown that the time-to-rupture is reduced in this liquid environment [1,2].This effect of liquid sodium has initiated a study of the creep and fatigue crack behaviour of this steel in the flowing liquid metal.Pre-cracked compact tension CT specimens of different sizes are used to study the influence of the liquid metal on the creep crack growth and the fatigue cracking behaviour.Int Journ of Fracture 32 (1986)

No abstract

In den Zeitstand-und LUkKontrAbb. 2. Aufbau der Teststrecke fiir Zeitstand-und Kriechversuche in strijmendem Natrium. Verglelchsversuche an LuftUrn den EMuB des strtimenden Natriums auf die mechanischen Kennwerte exakt ermitteln zu konnen, wurden in den Zeitstandanlagen des Instituts (3) Vergleichsversuche 'Oo0Abb. 5. Vergleich der Zeiten bis zum Einsetzen des tertilren f i ecbens in Natrium und in Luft (823 K). Abb. 8. Vergleich der minimalen Kriechgeschwindigkeiten in Natrium und in Luft (823 K). Natrium:log E = 20.4082 log a -56.3268(6) (E in s-l, a in MPa) Die Spannungsexponenten fur Luft (n = 17.86) und Natrium (n = 20.41) sind, allerdings auf der Basis weniger MeBpunkte Abb. 12. Bruchflachenmorphologie der Probe 24, links interkristalliner Anteil an der Bruchflache. Fig. 12. Morphology of the fracture of the specimen 24, intercrystalline part of the fracture on the left. und eines engen Bereichs der Spannung, geringfigig verschieden . Nachuntersuchungen an den ProbenDie Werte der Bruchdehnung sind -wie auch bei ahnlichen Werkstoffen (5) -durch Natrium reduziert, wie aus dem Diagramm der Abb. 9 zu ersehen ist. Diese Reduktion der Bruchdehnung ist durch den Ubergang vom transkristallinen Bruchverhalten an Luft zum interkristallinen Bruchverhalten in Natrium bedingt. Abb. 10