Oxide Dispersion Strengthened (ODS) steels are candidates for nuclear applications. ODS are produced by mechanical alloying of Fe-14Cr, Y2O3 and TiH2 powders and consolidation at 1100°C, resulting in finely dispersed nano-oxides. Their precipitation kinetics has been quantitatively determined by in-situ Small Angle X-ray Scattering during continuous heating up to 1100°C. Clusters, found in the as-milled state start growing at 450°C until 1100°C, while almost no coarsening was recorded during subsequent isothermal annealing. The nano-oxides resulting from these in-situ experiments were found to be representative of those in materials processed by hot isostatic pressing and hot extrusion.

HAL is a multi-disciplinary open access archive for the deposit and dissemination of scientific research documents, whether they are published or not. The documents may come from teaching and research institutions in France or abroad, or from public or private research centers. L'archive ouverte pluridisciplinaire HAL, est destinée au dépôt et à la diffusion de documents scientifiques de niveau recherche, publiés ou non, émanant des établissements d'enseignement et de recherche français ou étrangers, des laboratoires publics ou privés.