This paper reports the results of the synthesis of zeolitic material with adsorbent capacity from a rock of volcanic origin from sillar, Arequipa, Peru. The experimentation was carried out in a stainless steel reactor using solutions with different concentrations of KOH (2.0, 2.5 and 3.0 M), at a constant temperature of 150 ℃ and with a contact time between the volcanic material and the solution of 24, 48 and 72 h. The product obtained was characterized by means of scanning microscopic analysis (SEM) and cation exchange capacity (CIC).The results showed that synthetic zeolite was produced as a function of KOH concentration as the most influential independent variable. The highest cation exchange capacity (CEC) observed was 27.91 meq/100 g and corresponded to the formation of Linde F zeolite obtained with a 3.0 M KOH solution and for a time of 72 hours using a material whose particle size was 4 mm. Adsorption tests were performed using solutions containing Cu2+ cations in order to evaluate their adsorption capacity and kinetics.

Este artículo presenta los resultados de una investigación realizada sobre las formaciones ignimbríticas en el área de Puno en el sureste de Perú, asociadas con el volcanismo terciario. La caracterización mineralógica, realizada mediante análisis difractométrico y microscopía electrónica de barrido reveló la presencia de heulandita junto con esmectita, cuarzo, mordenita, cristobalita y feldespato. El análisis de laboratorio realizado en muestras representativas del depósito investigado mostró una capacidad de intercambio catiónico (CIC) de aproximadamente 50 meq por 100 gramos de material zeolítico y un área de superficie específica, determinada mediante el método N2-BET, de aproximadamente 33,56 m2 / g . Las pruebas de capacidad de intercambio de cationes utilizando soluciones que contienen diferentes concentraciones de NH4 +, Pb+2, Cd+2, Cu+2, Zn+2 y Mn+2, consideradas individualmente, han mostrado el siguiente orden de selectividad: Pb+2> Cd+2> Cu+2> Zn+2> Mn+2> NH4 +. Además, para aumentar la capacidad de intercambio catiónico, el material zeolítico se pre-trató con una solución de NaCl 2N. Los resultados obtenidos demuestran la eficiencia del preacondicionamiento que produce un aumento sustancial en la capacidad de intercambio para todos los cationes examinados.

El presente artículo reporta los resultados de la síntesis de material zeolítico con capacidad adsorbente a partir de una roca de origen volcánico proveniente de sillar, Arequipa, Perú. La experimentación se efectuó en un reactor de acero inoxidable utilizando soluciones con diferentes concentraciones de KOH (2.0, 2.5 y 3.0 M), a una temperatura constante de 150°C y con un tiempo de contacto entre el material volcánico y la solución de 24, 48 y 72 horas. El producto obtenido se caracterizó mediante, análisis microscópico de barrido (SEM) y capacidad de intercambio catiónico (CIC). Los resultados demostraron que se produjo zeolita sintética en función de la concentración de KOH como variable independiente más influyente. La mayor capacidad de intercambio catiónico (CIC) observada fue de 27.91 meq/100g y correspondió a la formación de zeolita Linde F obtenida con una solución de KOH 3.0 M y por un tiempo de 72 horas usando un material cuyo tamaño de partícula fue de 4 mm. Se realizaron pruebas de adsorción utilizando soluciones conteniendo cationes Cu2+ a fin de evaluar su capacidad y cinética de adsorción.