Cobalt-chromium layered double hydroxide (CoCr LDH), α- and β- Co(OH)2 and amorphous Cr(OH)3 have been synthesized under different reaction conditions. The obtained CoCr LDH was modified by stearic acid (SA) and sodium stearate (SS). The obtained samples have been characterized by X-ray diffraction (XRD), Scanning electron microscope (SEM), Ultraviolet-visible- (UV-Vis), Fourier transform infrared- (FTIR) and Energy-dispersive X-ray- (EDX) spectroscopy. The influence of reaction conditions on product composition, structural and optical properties of the samples have been discussed in detail. The basal spacing of CoCr-LDH increased from 7.366 Å to 7.428 Å and 25.214Å after the intercalation by stearic acid and sodium stearate, respectively. The average particles size by SEM analyze was estimated to be approximately 100–150 nm and 30–50 nm for CoCr-LDH0.6M(90°C) and CoCr-LDH0.6M(90°C)/SS nanostructures, respectively. Mixed hydroxides like α- and β- Co(OH)2 have been obtained along with LDH at lower pH value (pH ∼ 7). The number of diffraction peaks corresponding to β-Co(OH)2 has increased with relatively decreasing of Co2+ ions in the reaction medium. At high chromium concentrations (Co2+:Cr3+ = 1:3 and 1:5), amorphous Cr(OH)3 were formed in the experiment.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.