Fretting-corrosion is one of the main concerns in the application of hip prosthesis. This type of information is very important in the stage of orthopedic implants design, with the purpose of minimizing the amount of tissue exposed to corrosion products which are released during the permanence of the prosthesis in the patient. The residual corrosion products of stainless steels are associated to the occurrence of several adverse reactions in the human body. The knowledge about these corrosion products is extremely important in the phase of the project of hip prostheses, aiming at the minimization of the amount of exposure of the organic tissues to corrosion products released during the permanence of the prosthesis inside the patient.In the present work the mechanical stability and fretting corrosion resistance of modular hip prosthesis, which was fabricated with ASTM F 138 austenitic stainless steel, were evaluated according to the criteria of ASTM F 1875 standard, method I, which prescribes long term test, with the purpose of determining the amount of damage through the quantification of the corrosion products and debris which resulted from the fretting corrosion conditions. The mechanical tests were performed in a servohydraulic mechanical testing machine and the modular interfaces were exposed to an electrolytic 0.9% NaCl in distilled water solution and subjected to a minimum load of 230 N and a maximum load It can be concluded that the mass loss in the head-cone connection allowed the entrance of the physiological saline solution in the inner region of the head, increasing the predicted micro movement in the head-cone interface, resulting in an accelerated process of fretting-corrosion, and consequently the liberation of debris and corrosion products that could lead to adverse biological reactions.