No abstract

Catalyst-free graphene nano-sheets without substrates have been synthesized using fullerene and a high direct current (dc) pulse in the spark plasma sintering (SPS) process. Graphene nano-sheets were synthesized directly in the gas phase of carbon atoms which are generated from fullerene at a temperature of 600 o C. Characterization has been carried out by scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HR-TEM), Raman spectroscopy (Raman), X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD).

Stoichiometric and nonstoichiometric polyelectrolyte complex (PEC) was prepared with polyethylene glycol-monosuccinate (PEGMS), and chitosan (CS). A series of PEGMS were synthesized by a 1 : 1 mol ratio between PEG and succinic anhydride. Then, the novel PEC was prepared by a various mole reaction of the above synthesized PEGMS and CS. The physicochemical properties of the synthesized PEC was characterized by using elemental analysis, FTIR, 1 H, and 13 C nuclear magnetic resonance, dissolution behavior, and phase transition phenomenon. Furthermore, some properties of the PEC obtained were analyzed by UV-Visible spectrometry, wide-angle X-ray diffraction, differential scanning calorimeter, scanning electron microscope, and estimated solubility, and cell viability assay, respectively. It was found that the observed FTIR, 1 H, and 13 C-NMR data was in good agreement with the chemical structure of the prepared PEGMS and PEC. The dissolution behaviors of nonstoichiometric PEC were found to depend on the pH of the solution as well as on the PEGMS/CS composition. The study of MTT assay suggested that the viability of HepG2 human hepatoblastoma cell on PEC were increased significantly in accordance with mole ratio of CS. As the results, the obtained several product is a useful intermediate, which permits further chemical modification for the amino group of CS and may have potential applications in biocompatible or cosmetic systems.

In this study, the faunae before and after creating the Solbangjuk Wetland Ecological Park located in Jecheon-city were compared. As a result, the change of the fauna according to the creation of the park showed the phenomenon that the species having the strong wilderness are reduced and the rate of general species become higher. In addition, the species which receive the restrictions for moving such as mammals, amphibians and reptiles are being gradually decreased by the increased visitors owing to the creation of the park. Moreover because there was the case where group of fishes have died caused by discharging and working the water in the reservoir during the creation process of the park, the supplementation work for this is required. However, it showed that the insects sucking the honey from flowers in the composed flower garden after creating the park, and the aquatic insects which live in this park that the stable water system for the growth of wetland plants is maintained, are increased, respectively. As a result of this survey, because the reservoir for agriculture adjacent to the residential area is generally small, the securing of the habitat space for the wild animals living in this park when creating the ecological parks seems to be necessary. The countermeasure should be considered so that some areas of the reservoir can be maintained in their natural state by adjusting the visitors' trails and the position of facilities for in order to secure the habitat of the wild animals.

Electrospinning is a versatile process used to prepare micro or nano sized fibers from various materials dissolved in volatile solvents. This study reports electrospun pullulan fibrous webs fabricated through electrospinning using water as a solvent. The electrospinning conditions such as pullulan (PUL) concentration and applied voltage were optimized in order to obtain smooth electrospun fibers. The concentration of PUL greatly influenced the viscosity and surface tension of PUL solution. PUL beaded electrospun fibers were obtained from PUL solutions with concentrations lower than 5 wt%, while homogenous electrospun fibers were prepared from solutions with high concentration and high viscosity. The average diameters of PUL fibers were decreased to 200 nm when the polymer concentration was kept at 10 wt% and the applied voltage was fixed at 15 kV during electrospinning. PUL electrospun fiber exhibited higher solubility, flexibility, softness and adhesive strength.