Crystalline structure of a sample of Alumina (Al2O3 – reinforced epoxy) at (4% and 8%) has two prominent peaks at point (17°) and (19.5°) with miller vectors (111) and (220), respectively. These results are corresponding to crystalline cubic and notes growing of crystallization. The spectrum of (XRD) showed increase in crystalline size which means an increase in randomization and a lack of crystallization amorphous at (6%) (Al2O3). This result showed increase in crystalline size which means an increase in randomization and a lack of crystallization amorphous. Epoxy matrix reinforced by particles of silica (SiO2) and alumina (Al2O3) with different fractions were investigated for electrical properties such as dielectric constant, conductivity and dielectric loss index. This result showed effect of additional (SiO2, Al2O3) is small concentration except (2% SiO2) has large effect.

Thin films TiO2 prepared by thermal pyrolysis technique were examined for different thickness (75 to 375 step 75 nm). The results showed that the best transfer was 75 nm (89%), the allowable direct transfer calculation is equal to (3.4- 3.68 eV).

In the current study, a mathematical model using the MATLAB program was studied depending on the logistic power peak function to simulate the change in the absorbance with the different values of the concentrations of Rhodamine B. There are five parameters that have been applied to the concentration values of this laser dye that are proposed by the logistic power peak function of the seventh degree. To measure the absorption measurements, a range of concentrations from 4.7x10-7 to 3.76x10-6 M was prepared from Rhodamine B and dissolved in deionized water with a peak absorption at 556 nm. A JASCO V-630 spectrophotometer was used to record the spectra of the dye. The intensity is detected using a silicon photodiode (S1337). The results were found that the suggested function approved the relationship between the absorbance and the values of the concentrations with a significant accuracy depending on the high values of the correlation coefficients between the approximated original data which were determined more than 99.2%. The advantages of this function represent by providing parameters, which are used to describe the mathematical processes with high-resolution property profiles.