Abstract. In this article, the effect of nano-clay particles and heat-treating on thermo-mechanical fatigue (TMF) behaviors and failures of piston aluminum-silicon (AlSi) alloys was investigated. For this purpose, thermo-mechanical fatigue tests were conducted under out-of-phase (OP) loading conditions. Two loading conditions were checked based on different maximum temperatures (250, 300, and 350 °C) and various thermo-mechanical loading factors (100, 125, and 150%). The minimum temperature was constant in all tests at 50 °C under a heating/cooling rate of 10 °C/s and a dwell time of 5 s. Results showed that the nano-composites had a longer fatigue lifetime, at least 2 times higher, compared to the Al alloy, when the maximum temperature was 250 °C and the thermo-mechanical loading factor was 100%. However, no effective change was seen for the stress value and the plastic strain. At higher maximum temperatures, the change in the material behavior was lower. The fracture analysis by scanning electron microscopy (SEM) demonstrated that both materials had a brittle behavior due to cleavage and quasi-cleavage marks. The damage mechanism was also due to the Si-rich phase and intermetallics, respectively for the crack propagation and the micro-crack initiation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.