AIM:This study aimed to verify the influence of oral environment and denture cleansers on the surface roughness and hardness of two different denture base materials.METHODS:A total of sixteen identical removable disc specimens (RDS) were processed. Eight RDS were made from heat-cured acrylic resin (AR) and the other eight were fabricated from thermoplastic injection moulded resin (TR). Surface roughness and hardness of DRS were measured using ultrasonic profilometry and Universal testing machine respectively. Then the four RDS (two AR and two of TR) were fixed to each maxillary denture, after three months RDS were retrieved. Surface roughness and hardness of RDS have measured again.RESULTS:The surface roughness measurements revealed no significant difference (p >0.05) for both disc groups at baseline. However, both groups showed a significant increase in the surface roughness after three months with higher mean value for (TR) group. On the other hand, the (AR) group showed higher hardness mean value than (TR) group at baseline with no significant decrease in the hardness values (p >0.05) following three months follow-up period.CONCLUSIONS:Denture cleansers have an effect on the denture’s surface roughness and hardness concurrently with an oral condition which will consequently influence the complete dentures’ lifetime and patients’ satisfaction.

Objective:A comparative study between threaded and plain dental implant designs was performed to find out a new criterion for dental implant selection.Materials and Methods:Several dental implant designs with a systematic increase in diameter and length were positioned in a cylindrical-shaped bone section and analyzed using finite element method. Four loading types were tested on different dental implant designs; tension of 50 N, compression of 100 N, bending of 20 N, and torque of 2 Nm, to derive design curves.Results:Better stress distribution on both spongy and cortical bone was noted with an increase in dental implant diameter and length. With the increase in dental implant side area, a stress reduction in the surrounding bones was observed, where threaded dental implants showed better behavior over the plain ones.Conclusions:Increasing value of ratio between dental implant side area and its cross-sectional area reduces stresses transferred to cortical and spongy bones. The use of implants with higher ratio of side area to cross-section area, especially with weak jaw bone, is recommended.

Background This study aimed to evaluate the effect of mandibular complete dentures relining using soft relining material on the distribution of various occlusal forces using T-Scan system. Fifty completely edentulous patients having their conventional complete dentures earlier fabricated and utilized were selected for this study. Patients were controlled diabetics, characterized by having their residual alveolar ridges moderately developed and lined with firm mucoperiosteum. Mandibular complete dentures were relined with soft denture liner and T-Scan device was used for occlusal force distribution measurement prior to denture relining and three months thereafter the relinning procedure. Results Comparison between occlusal forces percentages before and after denture relining revealed that occlusal forces percentages was significantly lower after denture relining in anterior area, significantly higher after denture relining in right posterior area, where it was insignificantly higher after relining in left posterior area. Conclusions Our findings revealed that the use of soft denture liner for mandibular complete denture relining significantly improved the occlusal load distribution. Clinical trial registration Trial registration NCT, NCT04701970. Registered 23/11/2020—Retrospectively registered, https://clinicaltrials.gov/ct2/show/NCT04701970

No abstract