A new kind of the electromagnetic shielding composite coatings with high performance was prepared using the Ni-Cu-coated glass fibers and nickel powders as fillers and using epoxy resin as binder. The effects of the fibers on the conductivity and electromagnetic shielding effectiveness of the coatings were studied. The study results show as follows: 1) when the optimum ratio of the fillers to epoxy resin is 4:1, the coatings containing 6 wt% the Ni-Cu-coated glass fibers has best conductivity and electromagnetic shielding effectiveness; when the coating layer thickness is 300 μm, the shielding effectiveness of the coatings is up to 43.71-52.31 dB and increased an average of 13.94 dB compared with the nickel powders/ epoxy resin electromagnetic shielding coatings in the frequency range of 0.3-1000 MHz. This offers a new idea to enhance the added value of the glass fibers and the prevention of electromagnetic environmental pollution.

Electromagnetic radiation pollution and its protection has become one of the hot issues of urban development process. This paper analyzed the cause of natural and man-made electromagnetic environment pollution, pointed out the harm of public health and the city normal production and living order and the city sustainable development. This paper suggested that comprehensive treatment measures should be taken to solve the problem of electromagnetic environment pollution in cities including the reasonable planning and layout, the real powerful supervision, the advertisement and education, and the high level of protection technology. This plays an important role and realistic significance in building a harmonious urban electromagnetic environment.

0Cr18Ni9Ti stainless steels are used extremely broad, but the corrosion phenomena of 0Cr18Ni9Ti stainless steels will happen in its using because of various reasons. 0Cr18Ni9Ti stainless steels were taken with different process of heat treatment in order to change its corrosion resistance in this paper. The corrosion resistance performance of the samples was discussed by metallographic picture observation, weight-loss method and organizational analysis. The better heat treatment process was chosen, according to the contrast experiment method. The results indicate that the sample has the best corrosion resistance after 1040°C×1.5h solid solution and stabilization treatment of 890°C×2h. This study has certain positive meaning to improve the 0Cr18Ni9Ti stainless steel corrosion resistance.