In the yttrium aluminium system, the YAlO3 phosphor is a prominent host because of the yttrium aluminium ratio (1:1). Phosphor was synthesized by the solid-state reaction method at variable concentrations of erbium (0.1-2.5 mol%). This method is suitable for large-scale production and is a less time-consuming method when compared with the soft synthesis method. The prepared sample was characterized by X-ray diffraction technique and the crystallite size was calculated by Scherer's formula. Vibrational and bending analysis of prepared phosphor for optimized concentration of erbium ion is described based on the Fourier transform infrared spectroscopic technique. The photoluminescence (PL) emission spectra of prepared phosphor for variable concentrations of erbium ion were recorded and the excitation spectrum was found to be at 291 nm with three shoulder peaks at 305, 270 and 242 nm. For 291 nm excitation, the emission spectrum was found at 546 nm and 552 nm. PL intensity increased with increasing concentrations of erbium and after 2 mol% emission intensity decreased due to concentration quenching. Spectrophotometric determination of YAlO3:Er(3+) is described by CIE co-ordinates and shows an intense emission in the green region such that the prepared phosphor can act as a single host for green light emission. Thermoluminescence glow curve analysis of the YAlO3:Er(3+) phosphor was recorded for different ultraviolet (UV) light exposures and gamma exposure. Different gamma doses 0.5-2 kGy show a linear response. Kinetic parameters were calculated by the peak shape method.

No abstract

YAlO3: Sm(3+) phosphor has been synthesized by the solid state reaction method with calcium flouride used as a flux. The resulting YAlO3: Sm(3+) phosphor was characterized by X-ray diffraction (XRD) technique, Fourier transmission infrared spectroscopy (FTIR), photoluminescence . . PL excitation spectrum was found at 254,332,380,400,407, 603 and 713 nm. Under excitation of UV(713 nm) YAlO3: Sm(3+) (0-3 %) broad band emission were observed from 400 to 790 nm with a maximum around 713 nm of YAlO3 host lattice accompanied by weak emission of Sm(3+) ((4)G5/2 - (6)H5/2, (6)H7/2,(6)H9/2) transitions. The results of the XRD show that obtained YAlO3: Sm(3+) phosphor has a orthorhombic structure. The study suggested that Sm(3+) doped phosphors are potential luminescence material for laser diode pumping and inorganic scintillators.

No abstract