We prepared sulfonated polyphosphazenes having various aryloxy substituents, and studied their thermal stabilities and membrane properties. Sulfonated polyphosphazenes were synthesized by the reaction of polydichlorophosphazene with sodium aryloxides and subsequent sulfonation with fuming sulfuric acid. With increasing the degree of sulfonation, the polymers showed higher proton conductivity, but suffered more from swelling in an aqueous solution. We introduced a hydroxymethylphenoxy group onto the phosphazene backbone as a self‐crosslinkable group by reaction of poly(dichlorophosphazene) and a sodium salt of 4‐hydroxymethylphenol. When a film of a sulfonated polymer having a methylol group was heated at 80 °C under vacuum for 1 h, it became insoluble in NMP, indicating the formation of a network structure. We investigated the crosslinking reaction of the polymers by DSC and FTIR. The crosslinking reaction proceeded only in the sulfonated polymers. Because the sulfonated polymers provide acidic protons, the methylol groups became more electrophilic and reacted with neighboring aromatic rings. A condensation reaction between themselves could also occur. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 5850–5858, 2008

This study is investigated dose change on intra-oral radiography when same conditions under the others unit and same unit under the different exposed conditions. Three different radiation devices were studied. Exposure to the upper anterior, premolar and molar on the variant time and dose measure was using semiconductor radiation dose meter. Obtained film density value was analyzed to the belong in the range of diagnosis.Results for dose of each region were less dissimilar between the maximum and minimum. Its value was different 10 times as many as 3 times. In addition, the range of film density was 2.10 ∼ 2.95. These values were exceeded on the allow density of diagnostic value '0.25 ∼ 2.0'.Even if the same device and the same condition, measured dose was considerable differance and film density was showed show the inappropriate density range. Those can be caused the patient's re-take and patient's diagnostic errors so patients has affected direct and indirect radiological harm. Therefore, dental radiography devices will be required periodical maintenance and also provided standard on the exposure and processing conditions.