IRW(Inverter Resistance Welding) process and DSW(Delta-spot welding) process for dissimilar materials of DP590 and Al5052 were performed to evaluate the welding quality and mechanical properties. IRW experiment was carried out with changing the welding current. The other welding parameters such as pressure force, weld time, squeezing time and holding time were fixed. On the anther hand, DSW experiment was performed using the process tape at welding current of 11.5kA. The other conditions were same as IRW conditions. The various testes such as shear tensile strength, nugget diameters, EDS, SEM and cross-sectional observation for weld zone was performed. As a result, IMC(Inter Metallic Compound) thickness at 11.5kA was thinner than those of 9.5kA and 10.5kA conditions. In addition, thined IMC layer was observed when high electric current apply to the materials(DP590 and Al5052) in a short time throught dissimilar resistance spot welding controling welding conditions. The relationship between the thickeness of IMC and current intensity was after discussed.

In this research, magnesium powder was prepared by gas atomizing. Refinement behaviors of magnesium powder produced under different conditions were investigated using a mechanical milling (attrition milling) process. Analyses were performed to assess the characterization and comparison of milled powder with different steel ball sizes and milling times. The powders were analyzed by field emission scanning electron microscope, apparent density and powder fluidity. The particle morphology of the Mg powders changed from spherical particles of feed metals to irregular oval particles, then plate type particles, with an increasing milling time. Because of the HCP structure, deformation occurs due to the existence of the easily breakable C-axis perpendicular to the base, which results in producing plate-type powders. An increase in ball size and the impact energy of the magnesium powder maximizes the effect of refinement. Furthermore, it is possible to improve the apparent density and fluidity according to the smoothness of the surface of the initial powder.