The aim of this study was to identify the salivary components present in the pellicles formed on self-curing resin and to investigate the qualitative variations in adsorbed salivary pellicle compositions according to different exposure time to saliva. Experimental pellicles were formed by the incubation of polymerized resin particles with fresh human parotid or submandibular-sublingual saliva for either 20 min or 2 h. Pellicles were extracted using formic acid and lyophilized, they were then subjected to sodium dodecyl sulphate-polyacrylamide gel electrophoresis and immunoblotting to identify the adsorbed salivary components. The amino acid profiles of the 2 h-pellicles were analysed and compared with those of fresh glandular salivas. There was a difference in the 2 h-pellicle components on the self-curing resin compared with those of other dental materials as well as tooth enamel. The amino acid profiles of the 2 h-pellicles were also different from those of fresh glandular salivas. In the case of submandibular-sublingual saliva, the components of the 2 h-pellicle showed a different pattern compared with those of the 20 min-pellicle. However, there was no significant difference between the components of the 2 h- and 20 min-pellicles in the case of parotid saliva. A distinct difference was found in the surface binding affinities of immunoglobulin (IgA) from different glandular salivas. The findings of this study provide information concerning the initial bacterial adhesion on the surfaces of self-curing resin.

Objectives: This study investigated the effects of the color components of light-cured composite resin before and after polymerization on degree of conversion (DC) and biaxial flexural strength (FS). Materials and Methods: Four enamel shades (A1, A2, A3, A4) and two dentin shades (A2O, A3O) of Premisa (Kerr Co.) and Denfil (Vericom Co.) were evaluated on their CIE L*, a*, b* color components using the spectrophotometer before curing, after curing and at 7 day. The DC of same specimens were measured with Near-infrared spectrometer (Nexus, Thermo Nicolet Co.) at 2 hr after cure and at 7 day. Finally, the FS was obtained after all the other measurements were completed at 7 day. The correlations between each color component and DC and FS were evaluated. Results: The light-curing of composite resin resulted in color changes of Premisa in red-blue direction and Denfil in green-blue direction. The DC and FS were affected by product, time and shade (3-way ANOVA, p < 0.05) and product and shade (2-way ANOVA, p < 0.05), respectively. Premisa only showed a significant correlation between the DC and CIE a* component -before and after polymerization (Pearson product moment correlation, p < 0.05). The FS of Premisa showed significant negative correlations with CIE a* and CIE b* components. Conclusions: The DC and FS of the light-curing composite resin were affected by the color components of the material before and after polymerization.