The findings from this study confirm the role of diet-related exposure in the etiology of gastric cancer from the point of view of epidemiology. An increased risk of gastric cancer is associated with high intakes of protein, saturated fat, cholesterol and sodium, while consumption of polyunsaturated fat, vitamin A and ascorbic acid may have a protective effect against gastric cancer.

Hindered phenol exterminated hyperbranched polyester (mHBP) is fabricated by esterification reaction. The mHBP is introduced into nitrile rubber (NBR) to prepare NBR/mHBP blends. Structure, damping and mechanical properties of NBR/mHBP blends are investigated by Fourier transform infrared spectroscopy (FTIR), 1 H-NMR, dynamic mechanical thermal analyzer (DMTA), and tensile tester. FTIR spectra of the blends illustrate the intermolecular hydrogen bonding between the NBR and mHBP, contributing to the improvement of damping and mechanical properties. The results indicate that, with the increasing mHBP content, the T g of the blends shifted to a higher temperature with a broadening temperature range and improved mechanical properties, showing an application in adjusting the T g and temperature range without decreasing of loss factor. V C 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci.2015, 132, 42605.

A series of low viscosity acrylate‐based epoxy resin (AE)/glycol diglycidyl ether (GDE) systems were prepared. The effect of GDE and low molecular weight polyamide (LPA) content on the rheological behavior, phase structure, damping, and mechanical properties were studied by differential scanning calorimeter (DSC), viscometer, scanning electron microscopy (SEM), dynamic mechanical thermal analysis (DMTA), and electro mechanical machine. The viscosity of the uncured AE systems decreased significantly after the incorporation of GDE. The damping properties were found to decrease slightly with the increasing GDE and LPA content. The tensile strength of the cured AE/GDE samples enhanced significantly after the incorporation of GDE with at least 150% improvement for all the samples while it decreased slightly with increasing LPA content. The AE/GDE cured systems were intended for future use as structural damping materials. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016, 133, 42959.

No abstract

Acrylate-based epoxy resin (AE)/low molecular weight polyamine (LPA) composites were developed. The chemical structure, curing behavior, fracture morphology, damping properties, and mechanical properties were evaluated by Fourier transform infrared (FTIR), 1 H-nuclear magnetic resonance ( 1 H-NMR), gel permeation chromatography (GPC), Differential scanning calorimeter (DSC), scanning electron microscope (SEM), Dynamic mechanical thermal analysis (DMTA), and electro mechanical machine. Transmission electron microscope (TEM) and SEM pictures exhibited nanoscale micro-phase separation between epoxy and acrylic segmers. DMTA results indicated that the loss factor of cured AE/LPA system could reach 1.84 and temperature range of tan d > 0.5 was about 84 8C. Tensile strength and elongation at break of the cured AE samples can reach 6.5 MPa and 185%, respectively. V C 2016Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016, 133, 43654.