Amorphous polymers are heavily utilized materials in selective laser sintering (SLS) due to their good dimensional accuracy. However, sintered parts of amorphous polymers cannot be used as functional parts owing to their poor forming performance, including their low relative densities and tensile strength. Therefore, post-processing methods are employed to enhance the mechanical properties of amorphous polymers SLS parts without damaging their relatively high dimensional accuracy. In this study, the forming process of selective laser sintering (SLS) and post-processing on polystyrene (PS) was investigated. The orthogonal experiment was designed to obtain the optimal combination of process parameters. The effect of a single process parameter and the laser volumetric energy density (LVED) on dimension accuracy and warpage of the sintered parts were also discussed. In addition, a three-dimensional (3D) thermal model was developed to analyze the temperature fields of single-layer SLS parts and PS powder sintering mechanism. Then, infiltrating with epoxy resin was employed to enhance the mechanical properties of the PS parts. Good resin-infiltrated formulation was obtained based on the mechanical property tests and fractured surface analysis. This research provides guidance for SLS process and post-processing technology in polymers.

No abstract

Transparent hard and brittle (THB) materials have generated significant interest due to their excellent properties, such as wide spectral transmittance, heat resistance, chemical inactivity and high mechanical strength. To further explore the application of THB materials, it is inevitable to be confronted with a range of joining THB materials and THB material–metals. Ultrafast (UF) laser microwelding enables a new means of joining THB materials and THB material–metals, due to a localized energy deposition method, which is dominated by nonlinear absorption. This process can realize high-quality micro-zone direct joining of THB materials or THB material–metals without the assistance of a light-absorbing intermediate layer. In this paper, we review the advances in UF laser microwelding of THB materials and THB material–metals considering the last two decades, from the analysis of the interaction mechanism between UF laser and matter to the key influencing factors and practical applications of this technology. Finally, the existing problems and the future research focus of UF laser microwelding technology of THB materials and THB material–metals are discussed.