Direct splitting of water using a particulate photocatalyst would be a good way to produce clean and recyclable hydrogen on a large scale, and in the past 30 years various photocatalysts have been found that function under visible light. Here we describe an advance in the catalysis of the overall splitting of water under visible light: the new catalyst is a solid solution of gallium and zinc nitrogen oxide, (Ga(1-x)Zn(x))(N(1-x)O(x)), modified with nanoparticles of a mixed oxide of rhodium and chromium. The mixture functions as a promising and efficient photocatalyst in promoting the evolution of hydrogen gas.

“Waterproof” coats: Rh/Cr2O3 (core/shell) nanoparticles supported on a (Ga1−xZnx)(N1−xOx) solid solution are synthesized by an in situ photodeposition method. These nanoparticles (see picture) are used as a promoter for overall water splitting upon visible‐light irradiation (λ>400 nm). Without the Cr2O3 shell water is formed from H2 and O2 in an undesired back reaction.

The physical and photocatalytic properties of a novel solid solution between GaN and ZnO, (Ga(1-x)Zn(x))(N(1-x)O(x)), are investigated. Nitridation of a mixture of Ga(2)O(3) and ZnO at 1123 K for 5-30 h under NH(3) flow results in the formation of a (Ga(1-x)Zn(x))(N(1-x)O(x)) solid solution with x = 0.05-0.22. With increasing nitridation time, the zinc and oxygen concentrations decrease due to reduction of ZnO and volatilization of zinc, and the crystallinity and band gap energy of the product increase. The highest activity for overall water splitting is obtained for (Ga(1-x)Zn(x))(N(1-x)O(x)) with x = 0.12 after nitridation for 15 h. The crystallinity of the catalyst is also found to increase with increasing the ratio of ZnO to Ga(2)O(3) in the starting material, resulting in an increase in activity.