-Using the Siwek 20 L spherical explosion vessel, the explosion properties have been examined to understand the influence of magnesium content in Mg-Al alloy dusts with different concentration. For this purpose, the Mg-Al alloy dusts (volume mean diameter : 151~160 μm) with magnesium content ratio were used. As the results, the increase of Mg content in Mg-Al alloy causes an decreased minimum explosion concentration and an increased maximum explosion pressure. Also the maximum explosion pressure and maximum rate of pressure rise in Mg-Al alloy dusts mainly depended on the dust concentrations. However, for the explosion index (Kst) of Mg-Al (40:60 wt%), Mg-Al (50:50 wt%) and Mg-Al (60:40 wt%), it was founded to increase the Kst with increasing of magnesium content ratio.

The flash points of DMF based organic solvent mixtures used in the synthetic leather manufacturing process were measured. The test group was composed of seven types of solvent mixtures, which included DMF, toluene, and MEK. Each flash point was tested according to the international standard test methods of KS M 2010. The flash points were then predicted using some prediction models and compared with the measured data. From the analysis results, the binary mixtures with a mole ratio of less than approximately 0.7 showed that the measured values were under 25 ℃. This showed that the expectation for the flammable risk lowering effects due to the mixing of high flash point materials was reduced. In addition, the predicted values were evaluated using the average absolute deviation (A.A.D). The results showed that the Le Chatelier's models had an "A.A.D" of 1.95 ℃ and were the closest to the measured values.