Zinc oxide (ZnO) thin films have been prepared by ultrasonic Spray pyrolysis (USP) technique using zinc acetate dihydrate dissolved in methanol, ethanol and deionized water. A number of techniques, including X‐ray diffraction (XRD), scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy, UV–visible, electrical resistivity, and photoluminescence (PL) were used to characterize the obtained ZnO thin films. The evolution of the preferred crystalline orientations in the ZnO films was systematically investigated. The PL measurements indicated that the as‐grown ZnO thin films showed UV and green emission bands when they were excited by a Hg arc lamp using 313 nm as the excitation source. A red‐shift in the near band edge (NBE) has been observed with the increase in the substrate temperature and has been attributed to the compressive intrinsic stress present in the films. It is confirmed that oxygen vacancy (VO) is the most important factor that causes the broad visible emission. Furthermore, the visible emission and electrical resistivity of ZnO thin films are found to be a function of porosity. Also, it has been interestingly found that the intensity of green emission at ∼2.5 eV remarkably increased when the obtained ZnO films were deposited at 320 °C. The reason might be the VO, intrinsic stress, surface‐to‐volume ratio and porosity in the sample increased at low substrate temperature. The resistivity follows the same behavior as the intensity of the green emission. We propose a new luminescence mechanism based on the recombination related to oxygen vacancies in Zn‐rich or stoichiometric conditions. (© 2009 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.