Characterization of the UV oxidation for raw natural rubber (NR) was investigated in controlled conditions through image and FT-IR analysis. The UV oxidation was performed on a thin film of natural rubber coated on a KBr window at 254 nm and room temperature to exclude the thermal oxidation. Before or after exposure to UV light, image of the NR thin film was observed at a right or tilted angle. FT-IR absorption spectra were measured in transmission mode with the UV irradiation time. The UV oxidation of NR was examined by the changes of absorption peaks at 3425, 1717, 1084, 1477, 1377, and 833 cm −1 which were assigned to hydroxyl group (-OH), carbonyl group (-C=O), carbon-oxygen bond (-C-O), methylene group (-CH 2 -), methyl group (-CH 3 ), and cis-methine group (cis-CCH 3 =CH-), respectively. During the initial exposure period, the results indicated that the appearance of carbonyl group was directly related to the reduction of cis-methine group containing carbon-carbon double bond (-C=C-). Most of aldehydes or ketones from carbon-carbon double bonds were formed very fast by chain scission. A lot of long wide cracks with one orientation at regular intervals which resulted in consecutive chain scission were observed by image analysis. During all exposure periods, on the other hand, it was considered that the continuous increment of hydroxyl and carbonyl group was closely related to the decrement of methylene and methyl group in the allylic position. Therefore, two possible mechanisms for the UV oxidation of NR were suggested.

No abstract

ABSTRACT：More than 3 wt% of polycyclic aromatics (PCAs) in process oil is known to cause skin cancer. The criterion of distinguishing between low PCA oil and high PCA oil is based on 3 wt% of PCA. High PCA oil is called as a carcinogen like distillate aromatic extract (DAE). Low PCA oil is considered as safety oils like treated distillate aromatic extract (TDAE), mild extract solvate (MES), and paraffinic oil. Four types of process oils such as DAE, TDAE, MES, and paraffinic oil purified by solvent extraction and separation skills from SBR vulcanizates were measured by FT-IR techniques. The effects of rubber chemicals such as N-1,3-dimethylbutyl-N'-phenyl-p-phenylnenediamine (HPPD), polymerized 2,2,4-trimethyl-1,2-dihydroquinoline (TMDQ), paraffin wax as antidegradants, and processing aid like Structol 40MS on paraffinic oil from SBR vulcanizates were also studied. The type of low or high PCA was identified by the relative abundance of absorbance at the aromatic substitution patterns of 864, 810, and 754 cm -1 and at the paraffinic or naphthenic pattern of 721 cm -1 . 요 약：공정오일

No abstract