The system PPO/decalin was invastigated by wide-angle X-ray diffraction method. The polymer was used in i t s powder form. The experimental conditions were chosen to obtain maximum swelling of samples. I t was observed that ordering changes were taking place in a relatively short period of time after swelliiig. The degree of ordering was calculated for the swollen and dried samples. The observed relationships allowed conclusion concerning the influence of the swelling agent and conditions on the morphological changes in the studied system. Kontgenographische Untersuchung der strukturelleii ;hderurigeii irn System I'o1y(2,6-dirnelhyl-.f,4-pherc yleti)oxid/Deculin wahrend des QuellungsprozessesDas System PPO/Decalin wurde niittels Riintgeirweitwinkelstreuung untersucht. Das Polymer wurde in Pulverhrm eingesetzt, und die experimentellen Bedingungen wurden so gewiihlt, dalj maximale Quellung auftrat. Die Anderungen der Ordnung erfolgen in relativ kurzer Zeit. Der Ordnungsgrad der gequollenen ur,d der getrockneten Proben wurde berechnet. Aus. den EJgebnissen konnen SchluBfolgerungen iiber den KinfluD des Quellrnittels und der Quellbedingungen auf morphologische Anderungen in dem untersuchten System gezogen werden. Penmzenozpa$usecicue uccnedoeanus U~J C~H~H U R cmpyicmypbc e cucmeJue nonu(2,6-auflernun-1 ,4-$enunen)oiccuddeicaaun eo @ p e a s npoqecca na6yxanus

Act= Polymerica 36 (1905) Nr. 9 483 Strukturelle Besonderheiten und einige physikalisch-chemische Eigenschaften von aus nichtwaprigen Lcisungen erhaltenen Mischungen oon Cellulose und synthetischen Polymeren. 2. Hochauflcisende 13C-NMR von Mischungen aus Cellulose und synthetischen Polymeren im festen Zustund Mit Hilfe der hochauflosenden 13C-NMR-Spektroskopie wurden Mischungen von Cellulose mit Polymethylmethacrylat, Polyacrylnitril, Polyvinylacetat, Polyvinylalkohol und Polydimethylsiloxan mit unterschiedlicher quantitativer Zusammensetzung untersucht.