The modification and tailoring the characteristics of nanostructured materials are of great interest due to controllable and unusual inherent properties in such materials. A simple spray pyrolysis technique is used to prepare pure and La-doped ZnO films. The influence of La concentration (0, 0.33, 0.45, 0.66, 0.92 and 1.04 at. %) on the structural, optical, and magnetic properties of ZnO was investigated. The exact nominal compositions of the prepared films were determined from the field emission scanning electron microscope occupied with EDX. X-ray diffraction confirmed that the samples possessed single-phase hexagonal wurtzite structure. The main crystal size was decreased from 315.50 Å to 229.04 Å depending on La dopant concentration. This decrease is due to the small ionic radius of Zn ions in compared to La ions.The band gap values were found to be depend strongly on La 3+ ion content. Introducing La into ZnO induces a clear magnetic moment without any distortion in the geometrical symmetry, it 2 also reveals the ferromagnetic coupling. The saturation magnetic moment of 1.04 at% La-doped ZnO shows the highest value of 0.014 emu, which is ~23 times higher than pure ZnO sample.The obtained results were discussed and compared with other literature data and showed an acceptable agreement.

In this study the electrical properties of organic semiconductor orange nitrogen dye (OND) have been examined. Thin film samples were deposited from OND solution in water on a nickel substrate (it was the first electrode) at room temperature at different gravity conditions including, 1 g (reference samples), 123 g, 277 g and 1107 g by a centrifugal machine. As a second electrode of the samples a gallium drop was used. The voltage-current characteristics of the samples were measured at temperature interval of 30°C –- 60°C. It was found that all voltage-current characteristics were asymmetrical with slightly rectification behavior. The resistances of the samples decrease monotonously with temperature but with acceleration they show minimum around of 123 g. As a rule the forward bias resistance ("+"” voltage was applied to gallium) were less than reverse bias ones ("“+"” voltage was applied to nickel). The electric behavior of the samples analyzed by the conception of space-charge limited currents (SCLC) at the presence of two different kinds of metallic electrodes (Ni and Ga) in the samples.