This study examines the effect of high-velocity oxy-fuel (HVOF) coatings of Inconel, aluminum, and Colmonoy on the corrosion resistance of stainless steel substrates. The coated samples were characterized using SEM, XRD, and EDS techniques. Impedance and Tafel tests were used to investigate the coatings corrosion responses at 40, 50, and 60 °C. Inconel-coated specimens showed superior corrosion behavior thanks to the Cr2O3 layers formed between the lamella structures of the coating, preventing chloride ions from diffusing across the coating. Although the Nyquist curve indicated oxide layer formation for the Al-coated sample, the Tafel test results showed severe corrosion.