The relaxation propertics of the epoxy dian polymer ED-16 plastified with maleic anhydride were studied in the wide range of temperature from -150°C to + 500°C. The experimentally found great number of relaxation transitions are connected with the complex structure of the polymer and with tlie existence of A large nuniber of different forms of molecular motion. The observed rclaxations are classified and their characteristic constants (activation energy and preexponential factor) are given. A nonsegmental mechanism of the process of glass transition in highly crosslinked polymers is suggested. Relaxationseigenschaften eines mil Maleinsdureanhydrid plastifizierten EpoxidpolgmersDie Relaxationseigensehaften des mit hIaleinsiiureanliyclrid plas tifizierten Epoxydianpolymers E D-16 wurden i n dem Tcmperaturbercicli von -150OC bis + 5OOOC untersuclit. Die experimentell gefundene groDe Zahl von Relasationsubcrgiingen hiingt mit der komplexen Struktur des Polymers urid der Existenz einer groUen Zalil von unterschiedlichen molekularen Bewegungen zusammen. Die beobachtcten Relaxationsiibergiinge werden klassifiziert, und ihre eharakteristisehen Parameter (hktivicrungsenergie und priiexponen ticller Faktor) werden angegeben. Fur den Glasiibergang in liochvernc tzten Polymercn wird eiu nichtsegmcntalcr hIeehanismus angenornmen.

Für ein ungefülltes und mit technischem Ruß gefülltes Polybutadien‐Methylstyren‐Elastomer wurden die mechanischen Relaxationsspektren (innere Reibung) und die Strukturrelaxationsspektren (Wärmekapazität) miteinander verglichen. Es wird gezeigt, daß die nach beiden Methoden gefundenen Relaxationsübergänge übereinstimmen.

No abstract

No abstract