A nanocomposite material, composed of nano-sized MgO-filler added to a low-density polyethylene (LDPE), was subjected to electrical property investigations under DC voltage application. The volume resistivity of LDPE, under 40-80kV/mm DC field at 90°C, increases by the power of 10 due to the addition of only a few percent of nano-filler. The amount of space charge in LDPE under high electric field is reduced and the ratio of stress enhancement by space charge becomes less due to the addition of nanosized MgO-filler. The DC breakdown strength of LDPE is increased by adding nano-sized MgO-filler. Based on these results, the mechanism where by the nano-sized MgO filler had improved DC characteristics of LDPE was discussed.