Light-weight nanocomposites filled with carbon nanotubes (CNTs) are developed for their significant potentials in electromagnetic shielding and attenuation for wide applications in electronics, communication devices, and specific parts in aircrafts and vehicles. Specifically, the introduction of a second phase into/onto CNTs for achieving CNT-based heterostructures has been widely pursued due to the enhancement in either dielectric loss or magnetic loss. In this work, ferroferric oxide (Fe(3)O(4)) was selected as the phase in multiwalled carbon nanotube (MWCNT)-based composites for enhancing magnetic properties to obtain improved electromagnetic attenuation. A direct comparison between the two-phase heterostructures (Fe(3)O(4)/MWCNTs) and polyaniline (PANI) coated Fe(3)O(4)/MWCNTs, namely, three-phase heterostructures (PANI/Fe(3)O(4)/MWCNTs), was made to investigate the interface influences of Fe(3)O(4) and PANI on the complex permittivity and permeability separately. Compared to PANI/Fe(3)O(4)/MWCNTs, Fe(3)O(4)/MWCNTs exhibited enhanced magnetic properties coupled with increased dielectric properties. Interfaces between MWCNTs and heterostructures were found to play a role in the corresponding properties. The evaluation of microwave absorption of their wax composites was carried out, and the comparison between Fe(3)O(4)/MWCNTs and PANI/Fe(3)O(4)/MWCNTs with respect to highly efficient microwave absorption and effective absorption bandwidth was discussed.

No abstract

The porous Fe 3 O 4 /carbon core/shell nanorods were fabricated via a three-step process. R-Fe 2 O 3 nanorods were first obtained, and R-Fe 2 O 3 /carbon core/shell nanorods were subsequently fabricated using glucose as a carbon source by a hydrothermal method, in which the thickness of the carbon coating was about 3.5 nm. Fe 3 O 4 /carbon core/shell nanorods were synthesized after an annealing treatment of the product above under a mixture of Ar/H 2 flow. After the H 2 deoxidation process, the Fe 3 O 4 core exhibited a character of porosity; the thickness of the carbon shell was decreased to about 2.5 nm, and its degree of graphitization was enhanced. The interesting core/ shell nanostructures are ferromagnetic at room temperature, and the Verwey temperature was about 120 K. Electromagnetic properties of the core/shell nanorodÀwax composite were investigated in detail. The maximum reflection loss was about À27.9 dB at 14.96 GHz for the composite with a thickness of 2.0 mm, and the absorption bandwidth with the reflection loss below À18 dB was up to 10.5 GHz for the absorber with the thickness of 2À5 mm. The excellent electromagnetic wave absorption properties of the porous Fe 3 O 4 /carbon core/shell nanorods were attributed to effective complementarities between the dielectric loss and the magnetic loss.