This study evaluates the thermal, morphological and mechanical behavior of polypropylene (PP) composite with different natural fibers. The fibers used were wood, sugarcane, bamboo, babassu, coconut and kenaf with and without coupling agent. The thermal, morphological and mechanical properties were evaluated, and a composite PP+GFPP (glass fiber) was used as reference. The interaction at the interface fiber-polymer matrix was studied by scanning electron microscopy (SEM) at the fractured surface of the composites, as expected the presence of maleic anhydride (MA) as coupling agent increasedthe interaction at the interface. The influence of natural fiber in the degree of crystallinity of the composites was evaluated by DSC analysis. The samples of PP+GFPP and PP+(PP-MA)+WF (wood flour) showed better temperature stability. PP+GF also presented superior flexural modulus. The thermal dynamic mechanical behavior was evaluated by DMA, a decrease in storage modulus with increasing temperature was observed, the PP+GF and the composite containing maleic anhydride and sugarcane fiber showed higher modulus. The natural fiber biocomposites studied, consistently presented lower flexural modulus and tensile strength than the reference composite, with and without the use of coupling agent. As expected the use of natural fibers lowered the density compared to the reference material.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.