Microfibrillated cellulose (MFC) obtained by disintegration of bleached softwood sulphite pulp in a homogenizer, was hydrophobically modified by surface silylation with chlorodimethyl isopropylsilane (CDMIPS). The silylated MFC was characterized by Fourier transform infrared spectroscopy (FT-IR), atomic force microscopy (AFM), transmission electron spectroscopy (TEM), X-ray photoelectron spectroscopy (XPS) and white light interferometry (WLI). The degree of surface substitution (DSS) was determined using Si concentrations from XPS survey scans, as well as deconvoluted peaks in high-resolution C1s XPS spectra. The DSS values obtained by the two methods were found to be in good agreement. MFC with DSS between 0.6 and 1 could be dispersed in a non-flocculating manner into non-polar solvents, TEM observations showing that the material had kept its initial morphological integrity. However, when CDMIPS in excess of 5 mol CDMIPS/glucose unit in the MFC was used, partial solubilization of the MFC occurred, resulting in a drop in the observed DSS and a loss of the microfibrillar character of the material. The wetting properties of films cast from suspension of the silylated MFC were also investigated. The contact angles of water on the films increased with increasing DSS of the MFC, approaching the contact angles observed on super hydrophobic surfaces for the MFC with the highest degree of substitution. This is believed to originate from a combination of low surface energy and surface microstructure in the films.

Microfibrillated cellulose (MFC) was prepared by disintegration of bleached softwood sulphite pulp through mechanical homogenization. The surface of the MFC was modified using different chemical treatments, using reactions both in aqueousand organic solvents. The modified MFC was characterized with fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM). Epoxy functionality was introduced onto the MFC surface by oxidation with cerium (IV) followed by grafting of glycidyl methacrylate. The length of the polymer chains could be varied by regulating the amount of glycidyl methacrylate added. Positive charge was introduced to the MFC surface through grafting of hexamethylene diisocyanate, followed by reaction with the amines. Succinic and maleic acid groups could be introduced directly onto the MFC surface as a monolayer by a reaction between the corresponding anhydrides and the surface hydroxyl groups of the MFC.

The properties of water-in-toluene emulsions stabilized solely by hydrophobized microfibrillated cellulose (MFC) were investigated. By varying the degree of surface substitution (DSS), the wettability of the MFC was altered. All emulsions prepared with MFC displayed excellent stability to coalescence. The stability to gravity-induced sedimentation increased with increasing MFC concentration, the highest stability being obtained with MFC of moderate hydrophobicity. Drop sizes increased with increasing DSS, with a corresponding decrease in stability to sedimentation. An increase in the toluene:water ratio at constant MFC concentration resulted in a decrease in the average drop size. For all emulsions, the polydispersity in drop size decreased with decreasing average drop diameter.

We have prepared potentially permanent antimicrobial films based on surface-modified microfibrillated cellulose (MFC). MFC, obtained by disintegration of bleached softwood sulfite pulp in a homogenizer, was grafted with the quaternary ammonium compound octadecyldimethyl(3-trimethoxysilylpropyl)ammonium chloride (ODDMAC) by a simple adsorption-curing process. Films prepared from the ODDMAC-modified MFC were characterized by Fourier transform infrared spectroscopy (FT-IR) and X-ray photoelectron spectroscopy (XPS) and tested for antibacterial activity against the Gram-positive bacterium Staphylococcus aureus and the Gram-negative bacteria Escherichia coli and Pseudomonas aeruginosa. The films showed substantial antibacterial capacity even at very low concentrations of antimicrobial agent immobilized on the surface. A zone of inhibition test demonstrated that no ODDMAC diffused into the surroundings, verifying that the films were indeed of the nonleaching type.