Palm fiber (PF) reinforced acrylonitrile butadiene styrene (ABS) composite matrix was prepared by employing Injection Moulding Machine (IMM). Palm fiber was collected from ten different trees of different age group from Comilla region in Bangladesh. Three sets of samples were prepared for three different wt% (5%, 10% and 20%) of fiber contents. The mechanical (tensile strength, flexural stress, micro hardness, Leeb's rebound hardness) and physical (bulk density and water absorption) properties were measured. The observed result reveals that the tensile strength (TS) and flexural stress (FS) were decreased with increasing fiber contents in the PF-ABS composites except 10% fiber content.
With the aid of Injection Moulding Machine (IMM) Palm fiber reinforced Acrylonitrile Butadiene Styrene (ABS) composites (PF-ABS) were prepared. Three sets of samples were prepared for three different wt% (5%, 10% and 20%) of fiber contents. Scanning Electron Microscopy (SEM), X-ray diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FTIR) experiments were performed to study the surface morphology, microstructure (if it crystalline or noncrystalline) and new bond formation after preparation of the composites. SEM pattern shows that after addition of palm fiber in PF-ABS composites the brittleness increased due to creation of voids in the composites except 10% fiber content in PF-ABS. From XRD pattern it is clear that the palm fiber, ABS and PF-ABS composites are amorphous in nature. Moreover FTIR spectrum shows that there is no new bond formed after addition of palm fiber in ABS polymeric matrix to create PF-ABS composites.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.