This research includes preparation (NR50/SBR50/Oyster Shell Powder OSP) composites while the loading ratio of OSP were 0, 5, 10, 15, 20, 25, 30, 40, 60, 80, 100 pphr. The examination of FTIR (Fourier Transform Infrared analysis) of some specimen composites were carried out and study the effect of calcium carbonate (Oyster Shell Powder OSP) grain size <225 μ on the rheological properties of (NR50/SBR50/OSP) composites with different loading ratio of (OSP). The device used to examine the characteristics is oscillating disc rheometer according ASTM D-2705 and temperature 185°C, pressure 10 bar and time 6 min. These rheological properties included the scorch time (ts2), cure time (tc90), viscosity, Maximum torque (MH), Minimum torque (ML) while the results of all these properties were decreasing with increase the loading ratio of OSP with or without C.B 10 pphr also all these properties were decreasing after addition C.B = 10 pphr for the same loading ratio of OSP except maximum and minimum torque at high loading ratio.
This present work, includes the preparation of rubber batches containing silicone rubber (SIR) (80pphr) and polyurethane (PU) (20pphr) with micro-lead powder in different loading, respectively (0,20.40,60,80,100,150,200,250,300pphr). The mechanical properties measured the device universal tensometer, such as tensile strength, elongation and modulus of elasticity, according standard specified of (ASTM D-412) were followed and the hardness property measured by (Hardness Shore A) was put through its steps according to the standard specification (ASTMD-1415). The results were selected, and the sample (10) consisting of (SIR 80/PU20 and micro-lead 300pphr) was chosen because it is more suitable for the required mechanical properties. The results observed that the ratios of micro-lead loading increased, the tensile and elongation decreased, and the hardness and elastic modulus increased. Rubber batches reinforced with micro-lead were exposed to an infrared (FTIR) test device with the addition of hexane, where there were no changes in the infrared spectrum of the rubber composites (SIR80/PU20/Micro-Pb). Sample No. (10) was shown that the scanning electron microscope (SEM) before and after adding hexane, where it was noted that the image (A) without hexane, the absence of homogeneity of lead. As for image (B) in the presence of hexane, we note the homogeneity of lead and the distribution of lead equally, so that radiation examination were measured the Geiger counter of two sources of radioactive elements were used, the caesium source Cs137 and the cobalt source Co60. The radiation is attenuated through the material, while the thickness of the half (X1/2) gradually contrasts according to the attenuation of the radiation. This work is applied in the applications of shields as a protective suit against harmful radiation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.