Montmorillonite modified with distearyldimethyl ammonium chloride (C18-QAC) (Nanofil-15) (NF15) was incorporated into polydimethylsiloxane-urea (silicone-urea, PSU) copolymers. PSU was obtained by the reaction of equimolar amounts of aminopropyl terminated polydimethylsiloxane (PDMS) oligomer (=3,200 g/mol) and bis(4-isocyanatohexyl)methane (HMDI). A series of PSU/ NF15 nanocomposites were prepared by solution blending with organoclay loadings ranging from 0.80 to 9.60% by weight, corresponding to 0.30 to 3.60% C18-QAC. Colloidal dispersions of organophilic clay (NF15) in isopropanol were mixed with the PSU solution in isopropanol and were subjected to ultrasonic treatment. Composite films were obtained by solution casting. FTIR spectroscopy confirmed that the organoclay mainly interacted with the urea groups but not with PDMS. XRD analysis showed that nanocomposites containing up to 6.40% by weight of organoclay had fully exfoliated silicate layers in the polymer matrix, whereas 9.60% loading had an intercalated structure. Physicochemical properties of nanocomposites were determined. PSU/NF15 nanocomposites displayed excellent long-term antibacterial properties against E. coli.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.