Praseodymium sulfate was obtained by the precipitation method and the crystal structure was determined by Rietveld analysis. Pr2(SO4)3 is crystallized in the monoclinic structure, space group C2/c, with cell parameters a = 21.6052 (4), b = 6.7237 (1) and c = 6.9777 (1) Å, β = 107.9148 (7)°, Z = 4, V = 964.48 (3) Å3 (T = 150 °C). The thermal expansion of Pr2(SO4)3 is strongly anisotropic. As was obtained by XRD measurements, all cell parameters are increased on heating. However, due to a strong increase of the monoclinic angle β, there is a direction of negative thermal expansion. In the argon atmosphere, Pr2(SO4)3 is stable in the temperature range of T = 30–870 °C. The kinetics of the thermal decomposition process of praseodymium sulfate octahydrate Pr2(SO4)3·8H2O was studied as well. The vibrational properties of Pr2(SO4)3 were examined by Raman and Fourier-transform infrared absorption spectroscopy methods. The band gap structure of Pr2(SO4)3 was evaluated by ab initio calculations, and it was found that the valence band top is dominated by the p electrons of oxygen ions, while the conduction band bottom is formed by the d electrons of Pr3+ ions. The exact position of ZPL is determined via PL and PLE spectra at 77 K to be at 481 nm, and that enabled a correct assignment of luminescent bands. The maximum luminescent band in Pr2(SO4)3 belongs to the 3P0 → 3F2 transition at 640 nm.

The oxidation process of samariumoxysulfide was studied in the temperature range of 500–1000 °C. Our DTA investigation allowed for establishing the main thermodynamic (∆Hºexp = −654.6 kJ/mol) and kinetic characteristics of the process (Ea = 244 kJ/mol, A = 2 × 1010). The enthalpy value of samarium oxysulfate (ΔHºf (Sm2O2SO4(monocl)) = −2294.0 kJ/mol) formation was calculated. The calculated process enthalpy value coincides with the value determined in the experiment. It was established that samarium oxysulfate crystallizes in the monoclinic symmetry class and its crystal structure belongs to space group C2/c with unit cell parameters a = 13.7442 (2), b = 4.20178 (4) and c = 8.16711 (8)Å, β = 107.224 (1)°, V = 450.498 (9)Å3, Z = 4. The main elements of the crystalline structure are obtained and the cation coordination environment is analyzed in detail. Vibrational spectroscopy methods confirmed the structural model adequacy. The Sm2O2SO4luminescence spectra exhibit three main bands easily assignable to the transitions from 4G5/2 state to 6H5/2, 6H7/2, and 6H9/2 multiplets.

No abstract